BegoForm refractory post material for inlays, veneers and onlays. High edge strength posts, smooth and precise. Special ceramic masses of known manufacturers can be used for them.

Package:

• Set of 15 x 90g bags.

Product description:

• IPS PressVest Premium is a universal phosphate investment (type 1, class 1 and 2) that can be used with ceramic stamping materials in Ivoclar Vivadent furnaces.
• It can be used both in the speed heating procedure and in the conventional procedure.

"Speed" heat-up procedure:

• The ring is placed in a furnace heated to its final temperature and then transferred to a pressing furnace after a certain time.

Conventional annealing procedure:

• The ring is placed in a non-heated oven (room temperature) and heated to its final temperature as recommended. After the specified time, the ring is transferred to a pressing furnace.

Indications:

• IPS Press VEST Premium can be used with the following pressing ceramics for the Ivoclar Vivadent furnaces

• IPS e.max Press

• IPS e.max ZirPress
• IPS InLine PoM (Press- on Metal)

Storage:

• Store at 12-28 ° C
• Store the powder in a dry place
• Do not store the liquid at temperatures below +5 ° C (because of its sensitivity to low temperatures!). If the fluid freezes over, it becomes unusable due to crystallization.

Temperature at which the material can be used:

• Ambient temperature 18 ° C - max. 23 ° C.
• Temperature significantly deviating from this range may significantly affect the setting process.
• Lower ambient temperature slows down the chemical process.
• Higher ambient temperature accelerates the chemical process (from 23 - 28 ° C, the liquid with water can be cooled down to 12 ° C.

Mixing ratio:

• By diluting the liquid, it is possible to control the expansion of the investment material, which influences the fit of the pressed restoration. The concentration of the liquid is expressed in%. Important: The ratio of the amount of mixed liquid (liquid to investment material + distilled water) depends on the amount of powder and must be strictly adhered to.

• 100 g of powder: 26 ml of liquid (investment liquid + distilled water)

• 200 g powder: 52 ml liquid (investment liquid + distilled water)
• 300 g of powder: 78 ml of liquid (investment fluid + distilled water)

The following information on fluid concentrations is only a guide and may be adjusted according to the work size and mixing conditions. Do not dilute the fluid below 50%!

Package:

-100g.

Fluid for IPS PressVest Premium investment.

Package:

• 500ml.

Begoform investment fluid.

Package:

250 ml.

Fluid for IPS PressVest Premium investment

Package:

• 1l

TYPE 100 - liquid for the investment materials from Siladent.

Package:

• 1000 ml

Phosphate-bound, graphite-free, precision investment for all ceramic systems and high-speed pressed ceramics. Silavest Press can be used with ceramics pressed against metal and zircons.

Benefits:

• perfect match
• very smooth surface
• a fine-grained mass with a creamy consistency
• for all press ceramics systems
• easy released
• should be used with SILADENT type 100 expansion fluid.

Package:

• 100g

GC LiSi PressVest - liquid. Low temperature sensitive liquid - shipping in winter at the customer's risk.

Package:

• 900 ml.

Phosphate investment material used in the press ceramics technique. For the quick heating process.

Package:

60x100 g

Product description:

• IPS PressVest Premium is a universal phosphate investment (type 1, class 1 and 2) that can be used with ceramic materials for pressing in Ivoclar Vivadent furnaces.
• It can be used both in the speed heating procedure and in the conventional heating procedure.

"Speed" heating procedure:

• The ring is placed in a furnace heated to the final temperature and then, after a specified period of time, transferred to the pressing furnace.

Conventional heating procedure:

• The ring is placed in an unheated oven (room temperature) and heated to the final temperature as recommended. After a specified time, the ring is transferred to the pressing furnace.

Indications:

• IPS Press VEST Premium can be used with the following ceramic materials for pressing in Ivoclar Vivadent furnaces

• IPS e.max Press

• IPS e.max ZirPress
• IPS InLine PoM (Press-on Metal)

Storage:

• Store at a temperature of 12-28°C
• Store the powder in a dry place
• Do not store the liquid at a temperature lower than +5 °C (due to its sensitivity to low temperatures!). If the liquid freezes, it becomes unsuitable for use due to crystallization.

Temperature at which the material can be used:

• Ambient temperature 18 °C - max. 23 °C.
• Temperatures that deviate significantly from this range may significantly affect the setting process.
• Lower ambient temperature slows down the chemical process.
• A higher ambient temperature accelerates the chemical process (from a temperature of 23 - 28 °C, the liquid and water can be cooled to 12 °C.

Mixing proportions:

• As a result of diluting the liquid, it is possible to control the expansion of the investment material, which affects the fit of the pressed restoration. The concentration of the liquid is expressed in %. Important: The proportions of the amount of mixed liquid (liquid to investment material + distilled water) depend on the amount of powder and must be strictly observed.

• 100 g of powder: 26 ml of liquid (investment liquid + distilled water)

• 200 g of powder: 52 ml of liquid (investment liquid + distilled water)
• 300 g powder: 78 ml liquid (investment liquid + distilled water)

The following fluid concentration information is a guide only and may be adjusted based on job size and mixing conditions. Do not dilute the liquid below 50%!

Packaging:

• 50 x 100g.