Zirconium Explore Esthetic 98x12mm
Zirconium Explore Esthetic new generation zircon, up to 5 layers of multilayer translucency. Thanks to the increased strength in the gingival area and increased translucency in the enamel area, it allows for a very wide range of applications, while maintaining high aesthetics of the restoration.
parameters:
- Strength after sintering 727 MPa - 1000 MPa.
- Translucency 47% - 48.8%
- Sintering temperature 1480 °C
Application:
- foundations.
- crowns.
- 3-point bridges.
- Bridge with overhang (not recommended for patients with bruxism).
Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
Packaging:
- 1 piece
Zirconium Explore Hybrid 98x30mm + Gingiva 20ml
Discover tooth restoration with UPCERA Explore Hybrid.
Explore Hybrid disc with a diameter of 30 mm, designed to smoothly adapt to the natural structure of the teeth. Say goodbye to the limitations of typical gradient discs with Explore Hybrid. Effortlessly achieve light to dark pink gums. A solid base ensures durability and transparency. Thanks to Explore Hybrid, you will never lose the color of your gums again.
Sintering parameters:
- 1150°C 4°C/min 30 min
- 1300°C 2°C/min -1480°C 4°C/min 150min
- 800°C -8°C/min
- Open at 500°C
Packaging:
- 1 pc + Gingiva 20ml
Outlet Zirconium ST Color A3.5 AG 89-71-18 mm short expiry date
Zirconium ST Color A3.5 AG 89-71-18 mm - short expiry date.
Packaging:
- 1 piece
Zirconium HT White 98x10mm
Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
HT - High translucent
Characteristics:
- Recommended for foundations.
- Very high strength.
Destiny:
- Cap.
- Bridges.
- 3-4 point bridge.
- Bridge with overhang ((not recommended for patients with bruxism).
- Inlay bridge (not recommended for patients with bruxism).
- Maryland bridge (not recommended for patients with bruxism).
- Telescopic crown.
- Individual connectors.
Chemical composition:
- ZrO2 + HfO2 + Y2O3 - >99%
- Y2O3 - 4.5%~6%
- HfO2 - <5%
- Al2O3 - <0.5%
- Other oxides - <0.5%
Physical properties:
Density before sintering - 3.1+0.5g/cm3
Density after sintering - 6.08+0.01g/cm3
CTE (25- 500°C) 10.05+1.0×10- 6K- 1
Strength after sintering - 1300 Mpa
Percentage of monoclinic accelerated aging (%) - <15%
Average transparency - 39%
Cytotoxicity test - 0
Radioactivity - <0.1Bq/g
Sintering temperature - 1530°C
Packaging:
- 1 piece
Outlet Zirconium AG Explore Functional B1 89-71-16 short expiry date
Zirconium AG Explore Functional color B1 89-71-16 short expiry date.
Packaging:
- 1 piece
Outlet Zirconium AG ST Color D2 89-71-20mm short expiry date
Zirconium AG ST Color D2 89-71-20mm short expiry date.
Packaging:
- 1 piece
Outlet Zirconium AG ST Color D2 89-71-25mm short expiry date
Zirconium AG ST Color D2 89-71-25mm short expiry date.
Packaging:
- 1 piece
Outlet Zirconium ZZ Explore Functional B1 95x14mm
Zirconium ZZ Explore Functional color B1 95x14mm
Packaging:
- 1 piece
Zirconium HT White 38x12mm
Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
HT - High translucent
Characteristics:
- Recommended for foundations.
- Very high strength.
Destiny:
- Cap
- Bridges
- 3-4 point bridge
- Suspended bridge (not recommended for patients with bruxism).
- Inlay bridge (not recommended for patients with bruxism).
- Maryland bridge (not recommended for patients with bruxism).
- Telescopic crown.
- Individual connectors.
Chemical composition:
- ZrO2 + HfO2 + Y2O3 - >99%
- Y2O3 - 4.5%~6%
- HfO2 - <5%
- Al2O3 - <0.5%
- Other oxides - <0.5%
Physical properties:
Density before sintering - 3.1+0.5g/cm3
Density after sintering - 6.08+0.01g/cm3
CTE (25- 500°C) 10.05+1.0×10- 6K- 1
Strength after sintering - 1300 Mpa
Percentage of monoclinic accelerated aging (%) - <15%
Average transparency - 39%
Cytotoxicity test - 0
Radioactivity - <0.1Bq/g
Sintering temperature - 1530°C
Packaging:
- 1 piece
Zirconium HT White 98x14mm
Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
HT - High translucent
Characteristics:
- Recommended for foundations.
- Very high strength.
Destiny:
- Cap.
- Bridges.
- 3-4 point bridge.
- Suspended bridge (not recommended for patients with bruxism).
- Inlay bridge (not recommended for patients with bruxism).
- Maryland bridge (not recommended for patients with bruxism).
- Telescopic crown.
- Individual connectors.
Chemical composition:
- ZrO2 + HfO2 + Y2O3 - >99%
- Y2O3 - 4.5%~6%
- HfO2 - <5%
- Al2O3 - <0.5%
- Other oxides - <0.5%
Physical properties:
Density before sintering - 3.1+0.5g/cm3
Density after sintering - 6.08+0.01g/cm3
CTE (25- 500°C) 10.05+1.0×10- 6K- 1
Strength after sintering - 1300 Mpa
Percentage of monoclinic phase accelerated aging (%) - <15%
Average transparency - 43%
Cytotoxicity test - 0
Radioactivity - <0.1Bq/g
Sintering temperature - 1530°C
Packaging:
- 1 piece
Zirconium HT White 98x16mm
Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
HT - High translucent
Characteristics:
- Recommended for foundations.
- Very high strength.
Destiny:
- Cap
- Bridges
- 3-4 point bridge
- Suspended bridge (not recommended for patients with bruxism).
- Inlay bridge (not recommended for patients with bruxism).
- Maryland bridge (not recommended for patients with bruxism).
- Telescopic crown.
- Individual connectors.
Chemical composition:
- ZrO2 + HfO2 + Y2O3 - >99%
- Y2O3 - 4.5%~6%
- HfO2 - <5%
- Al2O3 - <0.5%
- Other oxides - <0.5%
Physical properties:
Density before sintering - 3.1+0.5g/cm3
Density after sintering - 6.08+0.01g/cm3
CTE (25- 500°C) 10.05+1.0×10- 6K- 1
Strength after sintering - 1300 Mpa
Percentage of monoclinic accelerated aging (%) - <15%
Average transparency - 39%
Cytotoxicity test - 0
Radioactivity - <0.1Bq/g
Sintering temperature - 1530°C
Packaging:
- 1 piece
Zirconium ST White 98x14mm Sale
Zirconium is a new line of materials based on zirconium oxide intended for use in CAD/CAM technology. Zirconium products are certified by SFDA, ISO13485, CE and FDA. Thanks to a two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconium discs.
ST-Super translucent
Characteristics:
- Recommended for work with full anatomical shape in the lateral section.
Destiny:
- Cap.
- Bridges.
- 3-4 point bridge.
- Bridge with suspension (not recommended for patients with bruxism).
- Bridge on inlays (not recommended for patients with bruxism).
- Maryland bridge (not recommended for patients with bruxism).
- Telescopic crown.
- Individual connectors.
Chemical composition:
- ZrO2 + HfO2 + Y2O3 - >99%
- Y2O3 - 4.5%~6%
- HfO2 - <5%
- Al2O3 - <0.5%
- Other oxides - <0.5%
Physical properties:
Density before sintering - 3.1+0.5g/cm3
Density after sintering - 6.08+0.01g/cm3
CTE (25- 500°C) 10.05+1.0×10- 6K- 1
Strength after sintering - 1300 Mpa
Percentage of monoclinical phaseaccelerated aging (%) - <15%
Average translucency - 43%
Cytotoxicity test - 0
Radioactivity - <0.1Bq/g
Sintering temperature - 1530°C
Packaging:
- 1 piece
Zirconium ST Color 98x10mm
Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
ST-Super translucent
Characteristics:
- Recommended for works in full anatomical shape in the posterior section.
Destiny:
- Cap.
- Bridges.
- 3-4 point bridge.
- Suspended bridge (not recommended for patients with bruxism).
- Inlay bridge (not recommended for patients with bruxism).
- Maryland bridge (not recommended for patients with bruxism).
- Telescopic crown.
- Individual connectors.
Chemical composition:
- ZrO2 + HfO2 + Y2O3 >98%
- Fe2O3 <0.3%
- Pr2O3 <0.3%
- Er2O3 <0.3%
- Other oxides <0.5%.
Physical properties:
- Density before sintering - 3.1+0.5g/cm3
- Density after sintering - 6.08+0.01g/cm3
- CTE (25- 500°C) - 10.05+1.0×10- 6K- 1
- Strength after sintering - 1300 MPa
- Percentage of monoclinic aging phase (%) <15%
- Cytotoxicity Test - 0 Level
- Radioactivity <0.1Bq/g
- Sintering temperature 1530°C
- Translucency 43%
Packaging:
- 1 piece
Zirconium ST Color 98x12mm
Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
ST-Super translucent
Characteristics:
- Recommended for works in full anatomical shape in the posterior section.
Destiny:
- Cap.
- Bridges.
- 3-4 point bridge.
- Suspended bridge (not recommended for patients with bruxism).
- Inlay bridge (not recommended for patients with bruxism).
- Maryland bridge (not recommended for patients with bruxism).
- Telescopic crown.
- Individual connectors.
Chemical composition:
- ZrO2 + HfO2 + Y2O3 >98%
- Fe2O3 <0.3%
- Pr2O3 <0.3%
- Er2O3 <0.3%
- Other oxides <0.5%.
Physical properties:
- Density before sintering - 3.1+0.5g/cm3
- Density after sintering - 6.08+0.01g/cm3
- CTE (25- 500°C) - 10.05+1.0×10- 6K- 1
- Strength after sintering - 1300 MPa
- Percentage of monoclinic aging phase (%) <15%
- Cytotoxicity Test - 0 Level
- Radioactivity <0.1Bq/g
- Sintering temperature 1530°C
- Translucency 43%
Packaging:
- 1 piece
Zirconium ST Color 98x14mm
Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
ST-Super translucent
Characteristics:
- Recommended for works in full anatomical shape in the posterior section.
Destiny:
- Cap.
- Bridges.
- 3-4 point bridge.
- Suspended bridge (not recommended for patients with bruxism).
- Inlay bridge (not recommended for patients with bruxism).
- Maryland bridge (not recommended for patients with bruxism).
- Telescopic crown.
- Individual connectors.
Chemical composition:
- ZrO2 + HfO2 + Y2O3 >98%
- Fe2O3 <0.3%
- Pr2O3 <0.3%
- Er2O3 <0.3%
- Other oxides <0.5%.
Physical properties:
- Density before sintering - 3.1+0.5g/cm3
- Density after sintering - 6.08+0.01g/cm3
- CTE (25- 500°C) - 10.05+1.0×10- 6K- 1
- Strength after sintering - 1300 MPa
- Percentage of monoclinic aging phase (%) <15%
- Cytotoxicity Test - 0 Level
- Radioactivity <0.1Bq/g
- Sintering temperature 1530°C
- Translucency 43%
Packaging:
- 1 piece
Zirconium HT White 98x18mm
Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
HT - High translucent
Characteristics:
- Recommended for foundations.
- Very high strength.
Destiny:
- Cap
- Bridges
- 3-4 point bridge
- Suspended bridge (not recommended for patients with bruxism).
- Inlay bridge (not recommended for patients with bruxism).
- Maryland bridge (not recommended for patients with bruxism).
- Telescopic crown.
- Individual connectors.
Chemical composition:
- ZrO2 + HfO2 + Y2O3 - >99%
- Y2O3 - 4.5%~6%
- HfO2 - <5%
- Al2O3 - <0.5%
- Other oxides - <0.5%
Physical properties:
Density before sintering - 3.1+0.5g/cm3
Density after sintering - 6.08+0.01g/cm3
CTE (25- 500°C) 10.05+1.0×10- 6K- 1
Strength after sintering - 1300 Mpa
Percentage of monoclinic accelerated aging (%) - <15%
Average transparency - 39%
Cytotoxicity test - 0
Radioactivity - <0.1Bq/g
Sintering temperature - 1530°C
Packaging:
- 1 piece
Zirconium ST Color 98x16mm
Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
ST-Super translucent
Characteristics:
- Recommended for works in full anatomical shape in the posterior section.
Destiny:
- Cap.
- Bridges.
- 3-4 point bridge.
- Suspended bridge (not recommended for patients with bruxism).
- Inlay bridge (not recommended for patients with bruxism).
- Maryland bridge (not recommended for patients with bruxism).
- Telescopic crown.
- Individual connectors.
Chemical composition:
- ZrO2 + HfO2 + Y2O3 >98%
- Fe2O3 <0.3%
- Pr2O3 <0.3%
- Er2O3 <0.3%
- Other oxides <0.5%.
Physical properties:
- Density before sintering - 3.1+0.5g/cm3
- Density after sintering - 6.08+0.01g/cm3
- CTE (25- 500°C) - 10.05+1.0×10- 6K- 1
- Strength after sintering - 1300 MPa
- Percentage of monoclinic aging phase (%) <15%
- Cytotoxicity Test - 0 Level
- Radioactivity <0.1Bq/g
- Sintering temperature 1530°C
- Translucency 43%
Packaging:
- 1 piece
Zirconium ST ML 98x14mm Sale!!!
Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
ST-Super translucent Multilayer.
Characteristics:
- Recommended for works in full anatomical shape.
- Super translucent
- Multilayer (layered).
Destiny:
- Cap.
- Bridges.
- 3-4 point bridge.
- Suspended bridge (not recommended for patients with bruxism).
- Inlay bridge (not recommended for patients with bruxism).
- Maryland bridge (not recommended for patients with bruxism).
- Telescopic crown.
- Individual connectors.
Chemical composition:
- ZrO2 + HfO2 + Y2O3 >98%
- Fe2O3 <0.3%
- Pr2O3 <0.3%
- Er2O3 <0.3%
- Other oxides <0.5%.
Physical properties:
- Density before sintering - 3.1+0.5g/cm3
- Density after sintering - 6.08+0.01g/cm3
- CTE (25- 500°C) - 10.05+1.0×10- 6K- 1
- Strength after sintering - 1300 MPa
- Percentage of monoclinic aging phase (%) <15%
- Cytotoxicity Test - 0 Level
- Radioactivity <0.1Bq/g
- Sintering temperature 1530°C
- Translucency 43%
Packaging:
- 1 piece
Zirconium TT Multilayered 98x14mm Sale!!!
Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
TT-Top translucent
Characteristics:
- Recommended for works in full anatomical shape in the anterior section
- the highest degree of enamel translucency
- guarantees a natural look
- available in 7 colors
Destiny:
- Cap
- 2 point bridges
- 3 point bridges
- Telescopic crown
- Individual connectors
- Veneers
chemical composition:
- ZrO2 + HfO2 86.3%~94.2%
- Y2O3 5.8%- 9.7%
- Fe2O3 <2%
- Er2O3 <0.5%
- Al2O3 <0.5%
- Other oxides <0.5%
Physical Properties:
- Density before sintering >2.8g/cm3
- Density after sintering 6.04+0.03g/cm3
- CTE (25- 500°C) 10.05+1.0×10- 6K- 1
- Strength after sintering >500 Mpa
- Percentage of monoclinic phase accelerated aging (%) <5%
- Chemical solubility after sintering <100ug/cm2
- 0 Level Cytotoxicity Test
- Radioactivity <0.1Bq/g
- Sintering temperature 1430~1470°C
Packaging:
1 piece
Zirconium HT White 98x20mm
Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
HT - High translucent
Characteristics:
- Recommended for foundations.
- Very high strength.
Destiny:
- Cap
- Bridges
- 3-4 point bridge
- Suspended bridge (not recommended for patients with bruxism).
- Inlay bridge (not recommended for patients with bruxism).
- Maryland bridge (not recommended for patients with bruxism).
- Telescopic crown.
- Individual connectors.
Chemical composition:
- ZrO2 + HfO2 + Y2O3 - >99%
- Y2O3 - 4.5%~6%
- HfO2 - <5%
- Al2O3 - <0.5%
- Other oxides - <0.5%
Physical properties:
Density before sintering - 3.1+0.5g/cm3
Density after sintering - 6.08+0.01g/cm3
CTE (25- 500°C) 10.05+1.0×10- 6K- 1
Strength after sintering - 1300 Mpa
Percentage of monoclinic accelerated aging (%) - <15%
Average transparency - 39%
Cytotoxicity test - 0
Radioactivity - <0.1Bq/g
Sintering temperature - 1530°C
Packaging:
- 1 piece
Zirconium HT ZZ 95x14mm
Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
HT - High translucent
Characteristics:
- Recommended for foundations.
- Very high strength.
Destiny:
- Cap
- Bridges
- 3-4 point bridge
- Suspended bridge (not recommended for patients with bruxism).
- Inlay bridge (not recommended for patients with bruxism).
- Maryland bridge (not recommended for patients with bruxism).
- Telescopic crown.
- Individual connectors.
Chemical composition:
- ZrO2 + HfO2 + Y2O3 - >99%
- Y2O3 - 4.5%~6%
- HfO2 - <5%
- Al2O3 - <0.5%
- Other oxides - <0.5%
Physical properties:
Density before sintering - 3.1+0.5g/cm3
Density after sintering - 6.08+0.01g/cm3
CTE (25- 500°C) 10.05+1.0×10- 6K- 1
Strength after sintering - 1300 Mpa
Percentage of monoclinic accelerated aging (%) - <15%
Average transparency - 39%
Cytotoxicity test - 0
Radioactivity - <0.1Bq/g
Sintering temperature - 1530°C
Packaging:
- 1 piece
Zirconium AG ST Color 89x71x16mm
Zirconium is a new line of materials based on zirconia designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconia discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
ST-Super translucent
Characteristics:
- Recommended for works in full anatomical shape in the posterior section.
Destiny:
- Cap.
- Bridges.
- 3-4 point bridge.
- Suspended bridge (not recommended for patients with bruxism).
- Inlay bridge (not recommended for patients with bruxism).
- Maryland bridge (not recommended for patients with bruxism).
- Telescopic crown.
- Individual connectors.
Chemical composition:
- ZrO2 + HfO2 + Y2O3 >98%
- Fe2O3 <0.3%
- Pr2O3 <0.3%
- Er2O3 <0.3%
- Other oxides <0.5%.
Physical properties:
- Density before sintering - 3.1+0.5g/cm3
- Density after sintering - 6.08+0.01g/cm3
- CTE (25- 500°C) - 10.05+1.0×10- 6K- 1
- Strength after sintering - 1300 Mpa
- Percentage of monoclinic aging phase (%) <15%
- Cytotoxicity Test - 0 Level
- Radioactivity <0.1Bq/g
- Sintering temperature 1530°C
- Translucency 43%
Packaging:
- 1 piece
Zirconium AG ST Color 89x71x14mm
Zirconium is a new line of materials based on zirconia designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconia discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
ST-Super translucent
Characteristics:
- Recommended for works in full anatomical shape in the posterior section.
Destiny:
- Cap.
- Bridges.
- 3-4 point bridge.
- Suspended bridge (not recommended for patients with bruxism).
- Inlay bridge (not recommended for patients with bruxism).
- Maryland bridge (not recommended for patients with bruxism).
- Telescopic crown.
- Individual connectors.
Chemical composition:
- ZrO2 + HfO2 + Y2O3 >98%
- Fe2O3 <0.3%
- Pr2O3 <0.3%
- Er2O3 <0.3%
- Other oxides <0.5%.
Physical properties:
- Density before sintering - 3.1+0.5g/cm3
- Density after sintering - 6.08+0.01g/cm3
- CTE (25- 500°C) - 10.05+1.0×10- 6K- 1
- Strength after sintering - 1300 Mpa
- Percentage of monoclinic aging phase (%) <15%
- Cytotoxicity Test - 0 Level
- Radioactivity <0.1Bq/g
- Sintering temperature 1530°C
- Translucency 43%
Packaging:
- 1 piece
Zirconium AG ST Color 89x71x12mm
Zirconium is a new line of materials based on zirconia designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconia discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
ST-Super translucent
Characteristics:
- Recommended for works in full anatomical shape in the posterior section.
Destiny:
- Cap.
- Bridges.
- 3-4 point bridge.
- Suspended bridge (not recommended for patients with bruxism).
- Inlay bridge (not recommended for patients with bruxism).
- Maryland bridge (not recommended for patients with bruxism).
- Telescopic crown.
- Individual connectors.
Chemical composition:
- ZrO2 + HfO2 + Y2O3 >98%
- Fe2O3 <0.3%
- Pr2O3 <0.3%
- Er2O3 <0.3%
- Other oxides <0.5%.
Physical properties:
- Density before sintering - 3.1+0.5g/cm3
- Density after sintering - 6.08+0.01g/cm3
- CTE (25- 500°C) - 10.05+1.0×10- 6K- 1
- Strength after sintering - 1300 Mpa
- Percentage of monoclinic aging phase (%) <15%
- Cytotoxicity Test - 0 Level
- Radioactivity <0.1Bq/g
- Sintering temperature 1530°C
- Translucency 43%
Packaging:
- 1 piece
Zirconium AG ST Color 89x71x18mm
Zirconium is a new line of materials based on zirconia designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconia discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
ST-Super translucent
Characteristics:
- Recommended for works in full anatomical shape in the posterior section.
Destiny:
- Cap.
- Bridges.
- 3-4 point bridge.
- Suspended bridge (not recommended for patients with bruxism).
- Inlay bridge (not recommended for patients with bruxism).
- Maryland bridge (not recommended for patients with bruxism).
- Telescopic crown.
- Individual connectors.
Chemical composition:
- ZrO2 + HfO2 + Y2O3 >98%
- Fe2O3 <0.3%
- Pr2O3 <0.3%
- Er2O3 <0.3%
- Other oxides <0.5%.
Physical properties:
- Density before sintering - 3.1+0.5g/cm3
- Density after sintering - 6.08+0.01g/cm3
- CTE (25- 500°C) - 10.05+1.0×10- 6K- 1
- Strength after sintering - 1300 Mpa
- Percentage of monoclinic aging phase (%) <15%
- Cytotoxicity Test - 0 Level
- Radioactivity <0.1Bq/g
- Sintering temperature 1530°C
- Translucency 43%
Packaging:
- 1 piece
Zirconium AG ST Color 89x71x20mm
Zirconium is a new line of materials based on zirconia designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconia discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
ST-Super translucent
Characteristics:
- Recommended for works in full anatomical shape in the posterior section.
Destiny:
- Cap.
- Bridges.
- 3-4 point bridge.
- Suspended bridge (not recommended for patients with bruxism).
- Inlay bridge (not recommended for patients with bruxism).
- Maryland bridge (not recommended for patients with bruxism).
- Telescopic crown.
- Individual connectors.
Chemical composition:
- ZrO2 + HfO2 + Y2O3 >98%
- Fe2O3 <0.3%
- Pr2O3 <0.3%
- Er2O3 <0.3%
- Other oxides <0.5%.
Physical properties:
- Density before sintering - 3.1+0.5g/cm3
- Density after sintering - 6.08+0.01g/cm3
- CTE (25- 500°C) - 10.05+1.0×10- 6K- 1
- Strength after sintering - 1300 Mpa
- Percentage of monoclinic aging phase (%) <15%
- Cytotoxicity Test - 0 Level
- Radioactivity <0.1Bq/g
- Sintering temperature 1530°C
- Translucency 43%
Packaging:
- 1 piece
Zirconium HT White 98x25mm
Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
HT - High translucent
Characteristics:
- Recommended for foundations.
- Very high strength.
Destiny:
- Cap
- Bridges
- 3-4 point bridge
- Suspended bridge (not recommended for patients with bruxism).
- Inlay bridge (not recommended for patients with bruxism).
- Maryland bridge (not recommended for patients with bruxism).
- Telescopic crown.
- Individual connectors.
Chemical composition:
- ZrO2 + HfO2 + Y2O3 - >99%
- Y2O3 - 4.5%~6%
- HfO2 - <5%
- Al2O3 - <0.5%
- Other oxides - <0.5%
Physical properties:
Density before sintering - 3.1+0.5g/cm3
Density after sintering - 6.08+0.01g/cm3
CTE (25- 500°C) 10.05+1.0×10- 6K- 1
Strength after sintering - 1300 Mpa
Percentage of monoclinic accelerated aging (%) - <15%
Average transparency - 39%
Cytotoxicity test - 0
Radioactivity - <0.1Bq/g
Sintering temperature - 1530°C
Packaging:
- 1 piece
Zirconium ST Color 98x18 mm
Zirconium is a new line of zirconium oxide materials designed for use in cad / cam technology. Zirconium products have SFDA, ISO13485, CE and FDA certificates. Due to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is an element characteristic of high-quality zirconium discs.
ST-Super translucent
Characteristics:
- recommended for fully anatomical work in the posterior region
Destiny:
- Cap
- Bridges
- 3- 4 point bridge
- Bridge with an evidence (not recommended for patients with bruxism)
- Bridge on inlays (not recommended for patients with bruxism)
- Maryland bridge (not recommended for patients with bruxism)
- Telescopic crown
- Individual connectors
Chemical composition:
- ZrO2 + HfO2 + Y2O3> 98%
- Fe2O3 <0.3%
- Pr2O3 <0.3%
- Er2O3 <0.3%
- Other oxides <0.5%.
Physical properties:
- Density before sintering - 3.1 + 0.5g / cm3
- Density after sintering - 6.08 + 0.01 g / cm3
- CTE (25- 500 ° C) - 10.05 + 1.0 × 10- 6K- 1
- Strength after sintering - 1100 Mpa
- Percentage of monoclinic phase aging (%) <15%
- Cytotoxicity testing - 0 Level
- Radioactivity <0.1Bq / g
- Sintering temperature 1530 ° C
Package:
1 piece.
Zirconium AG ST ML Color 89-71-14mm
Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
ST-Super translucent MT
Characteristics:
- Recommended for works in full anatomical shape.
- Super translucent.
- Available in 7 colors.
- Multilayer (layered).
Destiny:
- Cap.
- Bridges.
- 3-4 point bridge.
- Suspended bridge (not recommended for patients with bruxism).
- Inlay bridge (not recommended for patients with bruxism).
- Maryland bridge (not recommended for patients with bruxism).
- Telescopic crown.
- Individual connectors.
Chemical composition:
- ZrO2 + HfO2 + Y2O3 >98%
- Fe2O3 <0.3%
- Pr2O3 <0.3%
- Er2O3 <0.3%
- Other oxides <0.5%.
Physical properties:
- Density before sintering - 3.1+0.5g/cm3
- Density after sintering - 6.08+0.01g/cm3
- CTE (25- 500°C) - 10.05+1.0×10- 6K- 1
- Strength after sintering - 1300 Mpa
- Percentage of monoclinic aging phase (%) <15%
- Cytotoxicity Test - 0 Level
- Radioactivity <0.1Bq/g
- Sintering temperature 1530°C
- Translucency 43%.
Packaging:
- 1 piece
Outlet Zirconium AG ST Multilayered B1 89-71-14mm short expiry date
Zirconium AG ST Multilayered B1 89-71-14mm short shelf life.
Packaging:
- 1 piece
Zirconium HT ZZ 95x16mm
Zirconium is a new line of materials based on zirconia designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
- HT - High translucent
Characteristics:
- Recommended for foundations.
- Very high strength.
Destiny:
- Cap.
- Bridges.
- 3-4 point bridge.
- Suspended bridge (not recommended for patients with bruxism).
- Inlay bridge (not recommended for patients with bruxism).
- Maryland bridge (not recommended for patients with bruxism).
- Telescopic crown.
- Individual connectors.
Chemical composition:
- ZrO2 + HfO2 + Y2O3 - >99%
- Y2O3 - 4.5%~6%
- HfO2 - <5%
- Al2O3 - <0.5%
- Other oxides - <0.5%
Physical properties:
Density before sintering - 3.1+0.5g/cm3
Density after sintering - 6.08+0.01g/cm3
CTE (25- 500°C) 10.05+1.0×10- 6K- 1
Strength after sintering - 1300 Mpa
Percentage of monoclinic accelerated aging (%) - <15%
Average transparency - 39%
Cytotoxicity test - 0
Radioactivity - <0.1Bq/g
Sintering temperature - 1530°C
Packaging:
- 1 piece
Zirconium HT ZZ 95x12mm
Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
HT - High translucent
Characteristics:
- Recommended for foundations.
- Very high strength.
Destiny:
- Cap
- Bridges
- 3-4 point bridge
- Suspended bridge (not recommended for patients with bruxism).
- Inlay bridge (not recommended for patients with bruxism).
- Maryland bridge (not recommended for patients with bruxism).
- Telescopic crown.
- Individual connectors.
Chemical composition:
- ZrO2 + HfO2 + Y2O3 - >99%
- Y2O3 - 4.5%~6%
- HfO2 - <5%
- Al2O3 - <0.5%
- Other oxides - <0.5%
Physical properties:
Density before sintering - 3.1+0.5g/cm3
Density after sintering - 6.08+0.01g/cm3
CTE (25- 500°C) 10.05+1.0×10- 6K- 1
Strength after sintering - 1300 Mpa
Percentage of monoclinic accelerated aging (%) - <15%
Average transparency - 39%
Cytotoxicity test - 0
Radioactivity - <0.1Bq/g
Sintering temperature - 1530°C
Packaging:
- 1 piece
Zirconium HT ZZ 95x18mm
Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
HT - High translucent
Characteristics:
- Recommended for foundations.
- Very high strength.
Destiny:
- Cap
- Bridges
- 3-4 point bridge
- Suspended bridge (not recommended for patients with bruxism).
- Inlay bridge (not recommended for patients with bruxism).
- Maryland bridge (not recommended for patients with bruxism).
- Telescopic crown.
- Individual connectors.
Chemical composition:
- ZrO2 + HfO2 + Y2O3 - >99%
- Y2O3 - 4.5%~6%
- HfO2 - <5%
- Al2O3 - <0.5%
- Other oxides - <0.5%
Physical properties:
Density before sintering - 3.1+0.5g/cm3
Density after sintering - 6.08+0.01g/cm3
CTE (25- 500°C) 10.05+1.0×10- 6K- 1
Strength after sintering - 1300 Mpa
Percentage of monoclinic accelerated aging (%) - <15%
Average transparency - 39%
Cytotoxicity test - 0
Radioactivity - <0.1Bq/g
Sintering temperature - 1530°C
Packaging:
- 1 piece
Zirconium AG HT 89-71-14mm
Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
HT - High translucent
Characteristics:
- Recommended for foundations.
- Very high strength.
Destiny:
- Cap
- Bridges
- 3-4 point bridge
- Suspended bridge (not recommended for patients with bruxism).
- Inlay bridge (not recommended for patients with bruxism).
- Maryland bridge (not recommended for patients with bruxism).
- Telescopic crown.
- Individual connectors.
Chemical composition:
- ZrO2 + HfO2 + Y2O3 - >99%
- Y2O3 - 4.5%~6%
- HfO2 - <5%
- Al2O3 - <0.5%
- Other oxides - <0.5%
Physical properties:
Density before sintering - 3.1+0.5g/cm3
Density after sintering - 6.08+0.01g/cm3
CTE (25- 500°C) 10.05+1.0×10- 6K- 1
Strength after sintering - 1300 Mpa
Percentage of monoclinic accelerated aging (%) - <15%
Average transparency - 39%
Cytotoxicity test - 0
Radioactivity - <0.1Bq/g
Sintering temperature - 1530°C
Packaging:
- 1 piece
Zirconium ZZ ST Color 95x14mm
Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
- ST-Super translucent
Characteristics:
- Recommended for works in full anatomical shape in the posterior section.
Destiny:
- Cap.
- Bridges.
- 3-4 point bridge.
- Suspended bridge (not recommended for patients with bruxism).
- Inlay bridge (not recommended for patients with bruxism).
- Maryland bridge (not recommended for patients with bruxism).
- Telescopic crown.
- Individual connectors.
Chemical composition:
- ZrO2 + HfO2 + Y2O3 >98%
- Fe2O3 <0.3%
- Pr2O3 <0.3%
- Er2O3 <0.3%
- Other oxides <0.5%.
Physical properties:
- Density before sintering - 3.1+0.5g/cm3
- Density after sintering - 6.08+0.01g/cm3
- CTE (25- 500°C) - 10.05+1.0×10- 6K- 1
- Strength after sintering - 1300 MPa
- Percentage of monoclinic aging phase (%) <15%
- Cytotoxicity Test - 0 Level
- Radioactivity <0.1Bq/g
- Sintering temperature 1530°C
- Translucency 43%
Packaging:
- 1 piece
Zirconium AG ST 89-71-14mm
Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
ST-Super translucent
Characteristics:
- Recommended for works in full anatomical shape in the posterior section.
Destiny:
- Cap.
- Bridges.
- 3-4 point bridge.
- Suspended bridge (not recommended for patients with bruxism).
- Inlay bridge (not recommended for patients with bruxism).
- Maryland bridge (not recommended for patients with bruxism).
- Telescopic crown.
- Individual connectors.
Chemical composition:
- ZrO2 + HfO2 + Y2O3 - >99%
- Y2O3 - 4.5%~6%
- HfO2 - <5%
- Al2O3 - <0.5%
- Other oxides - <0.5%
Physical properties:
Density before sintering - 3.1+0.5g/cm3
Density after sintering - 6.08+0.01g/cm3
CTE (25- 500°C) 10.05+1.0×10- 6K- 1
Strength after sintering - 1300 Mpa
Percentage of monoclinic phase accelerated aging (%) - <15%
Average transparency - 43%
Cytotoxicity test - 0
Radioactivity - <0.1Bq/g
Sintering temperature - 1530°C
Packaging:
- 1 piece
Zirconium AG TT ML 89-71-16
Zirconium is a new line of zirconium oxide materials designed for use in cad / cam technology. Zirconium products have SFDA, ISO13485, CE and FDA certificates. Due to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is an element characteristic of high-quality zirconium discs.
TT-Top translucent ML
Characteristics:
- Recommended for fully anatomical work in the anterior region
- the highest degree of enamel translucency
- guarantees a natural look
Destiny:
- Cap
- 2 point bridges
- 3 point bridges
- Telescopic crown
- Individual connectors
- Veneers
Parameters:
- Strength after sintering 600 MPa
- Translucency 49%
- Sintering temperature 1450 degrees C
- The use of aesthetic restorations.
Package:
1 piece
Zirconium AG TT ML 89-71-16mm - Sale !!!
Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
TT-Top translucent ML
Characteristics:
- Recommended for works in full anatomical shape in the anterior section.
- The highest degree of enamel translucency.
- Guarantees a natural look.
Destiny:
- Cap.
- 2 and 3 point bridges in the anterior region.
- Telescopic crown.
- Individual connectors.
- Veneers.
Chemical composition:
- ZrO2 + HfO2 86.3%~94.2%
- Y2O3 5.8%- 9.7%
- Fe2O3 <2%
- Er2O3 <0.5%
- Al2O3 <0.5%
- Other oxides <0.5%
Physical Properties:
- Density before sintering >2.8g/cm3
- Density after sintering 6.04+0.03g/cm3
- CTE (25- 500°C) 10.05+1.0×10- 6K- 1
- Strength after sintering >600 MPa
- Percentage of monoclinic phase accelerated aging (%) <5%
- Chemical solubility after sintering <100ug/cm2
- 0 Level Cytotoxicity Test
- Radioactivity <0.1Bq/g
- Sintering temperature 1450°C
- Translucency 47%
Packaging:
- 1 piece
Zirconium Explore Functional 98x16mm
Zirconium Explore Functional, new generation zirconium, up to 5 layers of Multilayer translucency. Thanks to increased strength in the gingival area and increased translucency in the enamel area, it allows for a very wide range of applications while maintaining high aesthetics of the restoration.
Parameters:
- Strength after sintering 1027MPa - 1300MPa
- Translucency 43%- 46.6%
- Sintering temperature 1480 °C
Application:
- Foundations.
- Crowns.
- 3-point bridges.
- Multi-point bridges.
- Bridge with a suspension (not recommended for patients with bruxism).
Zirconium is a new line of materials based on zirconium oxide intended for use in CAD/CAM technology. Zirconium products are certified by SFDA, ISO13485, CE and FDA. Thanks to a two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconium discs.
Packaging:
- 1 piece
Zirconium Explore Functional 98x18mm
Zirconium Explore Functional, new generation zircon, up to 5 layers of Multilayer translucency. Thanks to increased strength in the gingival area and increased translucency in the enamel area, it allows for a very wide range of applications while maintaining high aesthetics of the restoration.
Parameters:
- Strength after sintering 1027MPa - 1300MPa.
- Translucency 43%- 46%
- Sintering temperature 1480 °C
Application:
- Foundations.
- Crowns.
- 3-point bridges.
- Multi-point bridges.
- Bridge with a suspension (not recommended for patients with bruxism).
Zirconium is a new line of materials based on zirconium oxide intended for use in CAD/CAM technology. Zirconium products are certified by SFDA, ISO13485, CE and FDA. Thanks to a two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconium discs.
Packaging:
- 1 piece
Zirconium Explore Esthetic 98x16mm
Zirconium Explore Esthetic new generation zircon, up to 5 layers of multilayer translucency. Thanks to the increased strength in the gingival area and increased translucency in the enamel area, it allows for a very wide range of applications, while maintaining high aesthetics of the restoration.
parameters:
- Strength after sintering 727MPa- 1000MPa
- Translucency 47% - 48.8%
- Sintering temperature 1480 °C
Application:
- foundations.
- Crowns.
- 3-point bridges.
- Overhang bridge (not recommended for patients with bruxism)
Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
Packaging:
- 1 piece
Zirconium Explore Esthetic 98x18mm
Zirconium Explore Esthetic new generation zircon, up to 5 layers of multilayer translucency. Thanks to the increased strength in the gingival area and increased translucency in the enamel area, it allows for a very wide range of applications, while maintaining high aesthetics of the restoration.
parameters:
- Strength after sintering 727MPa - 1000MPa
- Translucency 47% - 48.8%
- Sintering temperature 1480 °C
Application:
- foundations.
- crowns.
- 3-point bridges.
- Overhang bridge (not recommended for patients with bruxism)
Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconia discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
Packaging:
- 1 piece
Zirconium AG Explore Esthetic 89-71-18mm
Zirconium Explore Esthetic new generation zircon, up to 5 layers of multilayer translucency. Thanks to the increased strength in the gingival area and increased translucency in the enamel area, it allows for a very wide range of applications, while maintaining high aesthetics of the restoration.
parameters:
- Strength after sintering 727MPa - 1000MPa
- Translucency 47% - 48.8%
- Sintering temperature 1480°C
Application:
- foundations.
- Crowns.
- 3-point bridges.
- Overhang bridge (not recommended for patients with bruxism)
Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
Packaging:
- 1 piece
Zirconium AG Explore Functional 89-71-18mm
Zirconium Explore Functional new generation zircon, up to 5 layers of multilayer translucency. Thanks to the increased strength in the gingival area and increased translucency in the enamel area, it allows for a very wide range of applications, while maintaining high aesthetics of the restoration.
parameters:
- Strength after sintering 1027MPa - 1300MPa.
- Translucency 43% - 46.6%
- Sintering temperature 1480 °C
Application:
- foundations.
- crowns.
- 3-point bridges.
- Bridge with overhang (not recommended for patients with bruxism).
Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
Packaging:
- 1 piece
Zirconium TT One Multilayered 98x18mm Sale!!!
Highly aesthetic multilayer zirconia for universal use. Thanks to the increased strength (1000MPa), it allows you to make multi-unit bridges, while maintaining high aesthetics of the restoration (high translucency of 47%)
Technical data:
- Strength after sintering>1000 MPa
- Translucency 47%
- Sintering temperature 1480°C.
Application:
- foundations
- crowns
- 3 point bridges
Packaging:
- 1 piece.
Zirconium TT One Multilayered 98x22mm Sale!!!
Highly aesthetic multilayer zirconia for universal use. Thanks to the increased strength (1000MPa), it allows you to make multi-unit bridges, while maintaining high aesthetics of the restoration (high translucency of 47%)
Technical data:
- Strength after sintering>1000 MPa
- Translucency 47%
- Sintering temperature 1480 °C
Application:
- foundations.
- crowns.
- 3 point bridges.
Packaging:
- 1 piece.
Zirconium TT One Multilayered 98x25mm Sale!!!
Highly aesthetic multilayer zirconia for universal use. Thanks to the increased strength (1000MPa), it allows you to make multi-unit bridges, while maintaining high aesthetics of the restoration (high translucency of 47%)
Technical data:
- Strength after sintering>1000 MPa
- Translucency 47%
- Sintering temperature 1480 °C
Application:
- foundations.
- crowns.
- 3 point bridges.
Packaging:
- 1 piece.
Zirconium Explore Functional 98x20mm
Zirconium Explore Functional new generation zircon, up to 5 layers of multilayer translucency. Thanks to the increased strength in the gingival area and increased translucency in the enamel area, it allows for a very wide range of applications, while maintaining high aesthetics of the restoration.
parameters:
- Strength after sintering 1027MPa - 1300MPa.
- Translucency 43% - 46.6%
- Sintering temperature 1480 °C
Application:
- foundations.
- crowns.
- 3-point bridges.
- Multi-point bridges.
- Bridge with overhang (not recommended for patients with bruxism).
Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
Packaging:
- 1 piece
Zirconium AG ST Color 89-71-25mm Sale!!!
Zirconium is a new line of materials based on zirconium oxide intended for use in CAD/CAM technology. Zirconium products are certified by SFDA, ISO13485, CE and FDA. Thanks to a two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconium discs.
ST-Super translucent
Characteristics:
- Recommended for work with full anatomical shape in the lateral section.
Destiny:
- Cap.
- Bridges.
- 3-4 point bridge.
- Bridge with suspension (not recommended for patients with bruxism).
- Bridge on inlays (not recommended for patients with bruxism).
- Maryland bridge (not recommended for patients with bruxism).
- Telescopic crown.
- Individual connectors.
Chemical composition:
- ZrO2 + HfO2 + Y2O3 >98%
- Fe2O3 <0.3%
- Pr2O3 <0.3%
- Er2O3 <0.3%
- Other oxides <0.5%.
Physical properties:
- Density before sintering - 3.1+0.5g/cm3
- Density after sintering - 6.08+0.01g/cm3
- CTE (25- 500°C) - 10.05+1.0×10- 6K- 1
- Strength after sintering - 1300 Mpa
- Percentage of monoclinic phase aging (%) <15%
- Cytotoxicity test - 0 Level
- Radioactivity <0.1Bq/g
- Sintering temperature 1530°C
- Translucency 43%
Packaging:
- 1 piece
Zirconium ZZ ST Color 95x16mm
Zirconium is a new line of materials based on zirconium oxide designed for use in cad/cam technology. Zirconium products are SFDA, ISO13485, CE and FDA certified. Thanks to the two-stage production process: axial pressing and "cold" isostatic pressing, zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconia discs.
ST-Super translucent
Characteristics:
- Recommended for works in full anatomical shape in the posterior section.
Destiny:
- Cap.
- Bridges.
- 3-4 point bridge.
- Suspended bridge (not recommended for patients with bruxism).
- Inlay bridge (not recommended for patients with bruxism).
- Maryland bridge (not recommended for patients with bruxism).
- Telescopic crown.
- Individual connectors.
Chemical composition:
- ZrO2 + HfO2 + Y2O3 >98%
- Fe2O3 <0.3%
- Pr2O3 <0.3%
- Er2O3 <0.3%
- Other oxides <0.5%.
Physical properties:
- Density before sintering - 3.1+0.5g/cm3
- Density after sintering - 6.08+0.01g/cm3
- CTE (25- 500°C) - 10.05+1.0×10- 6K- 1
- Strength after sintering - 1300 MPa
- Percentage of monoclinic aging phase (%) <15%
- Cytotoxicity Test - 0 Level
- Radioactivity <0.1Bq/g
- Sintering temperature 1530°C
- Translucency 43%
Packaging:
- 1 piece
Zirconium zirconium discs for milling
Zirconium blocks are the most popular material for processing using CAD/CAM technology. Zirconium is a new line of materials based on zirconium oxide intended for use in CAD/CAM technology. Zirconium products are certified by SFDA, ISO13485, CE and FDA. Thanks to a two-stage production process: axial pressing and "cold" isostatic pressing, Zirconium zirconium discs are characterized by a homogeneous structure, which is a characteristic element of high-quality zirconium discs.
Characteristics:
- recommended for foundations
- very high durability
Destiny:
- Cap
- Bridges
- 3-4 point bridge
- Bridge with a suspension
- Bridge on inlays
- Maryland type bridge
- Telescopic crown
- Individual connectors.
Chemical composition:
- ZrO2 + HfO2 + Y2O3 - >99%
- Y2O3 - 4.5%~6%
- HfO2 - <5%
- Al2O3 - <0.5%
- Other oxides - <0.5%
Physical properties:
- Density before sintering - 3.1+0.5g/cm3
- Density after sintering - 6.08+0.01g/cm3
- CTE (25- 500°C) 10.05+1.0×10- 6K- 1
- Strength after sintering - 1400 Mpa
- Percentage of monoclinical phaseaccelerated aging (%) - <15%
- Average translucency - 43%
- Cytotoxicity test - 0
- Radioactivity - <0.1Bq/g
- Sintering temperature - 1400~1550°C